HIDROGEL NATRIUM ALGINAT-KITOSAN DENGAN METODE TAUT SILANG UNTUK PEMBALUT LUKA

Sridanti, Selvi (2019) HIDROGEL NATRIUM ALGINAT-KITOSAN DENGAN METODE TAUT SILANG UNTUK PEMBALUT LUKA. Skripsi thesis, Universitas Muhammadiyah Sukabumi.

[img] Text
COVER.pdf

Download (130kB)
[img] Text
LEMBAR PENGESAHAN PEMBIMBING.pdf

Download (200kB)
[img] Text
LEMBAR PERNYATAAN BEBAS PLAGIAT.pdf

Download (189kB)
[img] Text
BAB I.pdf

Download (136kB)
[img] Text
BAB II.pdf
Restricted to Repository staff only

Download (280kB) | Request a copy
[img] Text
BAB III.pdf
Restricted to Repository staff only

Download (198kB) | Request a copy
[img] Text
BAB IV.pdf
Restricted to Repository staff only

Download (505kB) | Request a copy
[img] Text
BAB V.pdf

Download (83kB)

Abstract

Hydrogel synthesis has been carried out Alginate-chitosan is applied to wound dressing. The synthesis of Sodium Alginate hydrogel and Chitosan hydrogel was also performed to compare the swelling ratio. Synthesis uses a cross link method, because with the cross link method it can produce hydrogels that have a swelling ratio and good hydrogel properties. Function group characterization was performed using FTIR and surface characterization using SEM and Antibacterial testing as one of the application requirements as wound dressing. The results of the swelling ratio of 8698% Sodium alginate hydrogel, Chitosan 678% hydrogel and the optimum Na.Alginat-Chitosan hydrogel at comparison (1: 1) had a swelling ratio of 746%. The FTIR results in sodium alginate hydrogel were obtained at 1624.06 cm-1 as COO- groups and CO groups at 1111.00 cm-1, chitosan hydrogels in 1568.13 cm-1 C = N bonds and in narium alginate-chitosan hydrogels there was sperm for COO-, CO and C = N. In SEM results, small pores are seen. In the antibacterial test results of Na.Alginat-Chitosan hydrogel, a inhibitory zone of 8.02mm was produced which entered into a less sensitive level as antibacterial.

Item Type: Thesis (Skripsi)
Uncontrolled Keywords: Hydrogel, Cross link, Sodium Alginate-Chitosan, Wound Dressing, Antibacterial.
Subjects: T Technology > T Technology (General)
Divisions: Fakultas Sains dan Teknologi > Kimia
Depositing User: Perpus ID UMMI
Date Deposited: 14 Mar 2019 08:19
Last Modified: 14 Mar 2019 08:19
URI: http://eprints.ummi.ac.id/id/eprint/819

Actions (login required)

View Item View Item